Perfect high-shine aluminium silver spray
METSRFSPR-(ALUSIVER-PERFECT)-400ML
Register now and access more than 125,000 products
High layer thickness with first spray coat
- Very safe due to optimal protection against the elements
- Minimal time required, as only one work step is necessary
- Provides good coverage
Versatile use thanks to adjustable spray head
Large-area and minor repairs can be carried out quickly and safely with the adjustable spray head.
High degree of resistance to running
High abrasion resistance
Not suitable as a primer for PU, MS polymer or hybrid sealing compounds.
Datasheets(X)
For visual enhancement, repair and protection against corrosion of metallic surfaces.
The base material must be clean, dry and free from grease. Remove rust and old loose paint, sand and clean. Vigorously shake the can for approx. 2 minutes before use.
Chemical basis | Ethyl cellulose synthetic resin |
Colour | Aluminium silver |
Contents | 400 ml |
Gloss level | High gloss |
Min. curing time | 4 h |
Max. curing time | 6 h |
Fully hardening/curing conditions | At recommended dry layer thickness |
Max. short-term temperature resistance | 400 °C |
Min. dust-drying time | 15 min |
Conditions for dust-drying time | at recommended dry layer thickness |
Recoatable/Can be painted over | Conditional, preliminary testing required |
Coating thickness | 7 µm |
Dry layer thickness (first back-and-forth motion) | 7 µm |
Propellant | Butane, Propane |
Ignition temperature | 235 °C |
Min. flashing point | -97 °C |
Shelf life from production | 24 Month |
Conditions to maintain shelf life from production | at 10°C to 25°C |
Min. grip strength | 25 min |
Grip strength conditions | at recommended dry layer thickness |
Cross-cut test | MAN 0-1 |
Cross-cut test conditions | in accordance with DIN 53151 |
AOX-free | Yes |
Spot weldable | No |
Substrates with good adhesion | Wood, Metal, Cardboard |
Select RAL-colour code
!! NOTE: On-screen visualisation of the colour differs from real colour shade!!