1C gun foam
1C gun foam B3
GUNFM-1C-B3-IVORY-750ML
Register now and access more than 125,000 products
Excellent adhesion to virtually all construction substrates (with the exception of PE, PP, PTFE and silicone)
Better sound and heat insulation properties than mineral wool, cork and fibreglass
Dimensionally stable
No volume shrinkage and only minimal post-expansion once the product has fully hardened.
Quick to fully harden
Fine-celled and uniform foam structure
Resistant to ageing
Resistant to a large number of solvents, paints and chemicals
Primer should be applied to porous and absorbent substrates. PURLOGIC® TOP can be applied with the PURLOGIC® Xpress, art. no. 08911524 and PURLOGIC® COMBIpress, art. no. 08911526 foam guns. Other guns are not compatible.
Datasheets(X)
Secure insulating and filling of window joints, pipe openings, joints, wall joints, wall openings and cavities, such as wall openings, roof finishings, pipe ducts, roller shutter boxes etc. Adheres to concrete, stone, hard PVC, metal and wood. Does not adhere to polyethylene, silicone, PTFE and grease.
Shake can vigorously 20 times before use. Substrates must be clean, solid and free from dust and grease. Pre-treat highly absorbent substrates. Adhesion surfaces must be moistened with water before the foam is applied. Moisten again if several foam beads are applied. Screw the can all the way into the gun can support - do not screw too far or tilt. Foam continues to expand after application. Immediately remove splashes of foam with PURlogic Clean, art. no. 0892160. Thoroughly clean the gun and valve after use. Always leave the open can screwed onto the gun.
Chemical basis | Moisture curing polyurethane prepolymer |
Colour | Yellow |
Smell/fragrance | Characteristic |
Moulded density | 25 kg/m³ |
Conditions for moulded density | in accordance with DIN EN ISO 845 (average) |
Tack-free after | 10 min |
Conditions for being tack-free | at 20°C and 65% humidity with 30-mm adhesive line |
Can be cut after | 40 min |
Conditions for ability to cut | at 20°C and 65% relative humidity at 30-mm adhesive line |
Final spreading possible after | 2 h |
Conditions for final spreading | at 20°C and 65% relative humidity at 30-mm adhesive line |
Full resilience | 12 h |
Conditions for full resilience | at 20°C and 50% relative humidity |
Min. processing temperature | 5 °C |
Max. processing temperature | 30 °C |
Min. surface processing temperature | 5 °C |
Max. surface processing temperature | 35 °C |
Min. temperature resistance | -40 °C |
Max. temperature resistance | 90 °C |
Building material class | B3 - Of high flammability |
Building material class conditions | in accordance with DIN 4102 |
Heat conductance λ | 0.032 W/(m*K) |
Heat conductance λ conditions | in accordance with DIN 52612 |
Compression strength | 0.3 N/mm² |
Compression strength conditions | in accordance with DIN 53421 |
Conditions for acoustic insulation of joints | in accordance with DIN 52210 |
Acoustic insulation for 10 mm-wide joint | -1 dB |
Acoustic insulation for 20 mm-wide joint | -6 dB |
Ultraviolet resistance | No |
Breaking elongation | 25 % |
Breaking elongation conditions | in accordance with DIN 53571 |
Flexural strength | 0.7 N/mm² |
Conditions for flexural strength | in accordance with DIN 53423 |
Shear strength | 0.17 N/mm² |
Conditions for shear strength | in accordance with DIN 53427 |
Yield (volume) approx. | 40 l |
Conditions for yield | Foam yield (free foaming) |
Contents | 750 ml |
Container | Can |
Weight of content | 735 g |
Shelf life from production | 12 Month |
Conditions to maintain shelf life from production | at 20°C |